INSTRUCTION FOR USE
GlassyCem (GIC) Luting Cement
Radiopaque glass ionomer luting cement
COMPOSITION
Calcium alumofluorosilicate radiopaque glass, polyacrylic acid, tartaric acid
PROPERTIES
Glass Ionomer cement GLASSYCEM contains modifiers and additives, controlling time and mechanism of paste formation.
Mixing of powder with liquid forms a plastic paste with film thickness 15 μm. After hardening forms a cement with high biocompatibility to hard tooth tissues, sufficient strength (130 MPa) and acid erosion resistance.
Polyaclylic acid binds with dentin calcium and provides chemical adhesion and marginal fit of cement to hard tooth tissues and main construction materials. Conditioning of hard tooth tissues surfaces improves cement adhesion. Fluorine-containing glass filler is able to accumulate and release fluorine ions, thus providing prolonged anticaries effect. Aesthetic properties of material allow to use it for fixation of metal-free crowns and bridges made of high-strength ceramics.
Conditioner — is a water solution of polyacrylic acid (12 %) of blue color. Surface conditioning significantly improves adhesion and ion exchange between tooth structure and glass ionomer cement.
INDICATIONS
Radiopaque glass ionomer cement GLASSYCEM is used for cementation of crowns, dental bridgework, inlays and onlays
CONTRAINDICATIONS
Drug idiosyncrasy
Use with great care for allergic
patient Don’t misuse
SIDE EFFECTS
As far as all terms of storing, transporting and application are observed, there are no side effects
PRESENTATION
Powder (jar) 20g/35g
Liquid (bottle) 16g/28g
Measuring spoon Mixing pad
Produced separately: Conditioner (bottle) 5ml
STORAGE
Store at the temperature from 5 °C to 25 °C. Keep in dry place.Tightly close container immediately after use,Keep away from humidity!,Do not use after expiry date,Shelf life — 3 years